Abstract

Highly abrasion-resistant transfer coatings are provided on a wide variety of substrates, thermoplastic or thermosetting, by transfer coating from a mold surface or a flexible web, such as by use of a heat transfer tape, an ultra-thin coating consisting essentially of a non-resinous binder material such as microcrystalline cellulose together with mineral abrasive particles, preferably alumina or a mixture of silica and alumina which have been heated together at a temperature of at least 140° F., the ultra-thin coating also preferably containing a silane and a small quantity of a sticking agent such as a thermoplastic or thermosetting resin.

Claims

What is claimed is: 1. A process for providing an abrasion-resistant deposit on the surface of a substrate, comprising providing a transfer carrier coated with an ultra-thin deposit consisting essentially of a non-resinous binder material, a small quantity of finely divided solid lubricant and mineral abrasive particles, which ultra-thin deposit has been dried on said transfer carrier at a temperature of at least 140° F., transferring said dried ultra-thin deposit from said transfer carrier to the surface of a substrate under conditions of heat and pressure whereby said deposit becomes adhered to said substrate, and removing said transfer carrier. 2. A process according to claim 1, wherein said carrier is a mold surface or a flexible web. 3. A process according to claim 1, wherein said binder material consists essentially of microcrystalline cellulose or a mixture of microcrystalline cellulose with a small quantity of carboxy methyl cellulose. 4. A process according to claim 1, wherein said ultra-thin deposit also contains a small quantity of a silane. 5. A process according to claim 1, wherein said ultra-thin deposit also contains up to about 35% by weight based on the total solids of a sticking agent or film-forming binder. 6. A process according to claim 3, wherein the ultra-thin deposit also contains a small quantity of a silane and up to about 35% based on the total weight of solids of a sticking agent or film-forming binder. 7. A process according to claim 6, wherein said sticking agent or film-forming binder is a thermoplastic or a thermosetting material. 8. A process according to claim 1, wherein said surface of said substrate is a thermosettable material, a thermoplastic, paper or a wood product. 9. A product obtained by the process of claim 1, wherein said substrate is a thermoset product other than a decorative laminate, a thermoplastic, paper or a wood product. 10. A product obtained by the process of claim 3, wherein said surface of said substrate is a thermosettable material, other than a decorative laminate a thermoplastic, paper or a wood product. 11. A product obtained by the process of claim 4, wherein said surface of said substrate is a thermosettable material, other than a decorative laminate a thermoplastic, paper or a wood product. 12. A product obtained by the process of claim 5, wherein said surface of said substrate is a thermosettable material, other than a decorative laminate a thermoplastic, paper or a wood product. 13. A heat transfer for carrying out the process of claim 1, wherein said transfer carrier is an impermeable, flexible web, said dried ultra-thin deposit being over said web and a plastic layer being over said dried ultra-thin deposit, said plastic layer serving as a base coating or an adhesive coating. 14. A heat transfer according to claim 13, wherein said binder material of said ultra-thin deposit consists essentially of microcrystalline cellulose or a mixture of microcrystalline cellulose with a small quantity of carboxy methyl cellulose. 15. A heat transfer according to claim 14, wherein the ultra-thin deposit also contains a small quantity of a silane. 16. A heat transfer according to claim 14, wherein the ultra-thin deposit also contains up to 35% by weight, based on the total weight of solids, of a sticking agent or film-forming binder. 17. A heat transfer according to claim 15, wherein the ultra-thin deposit also contains up to 35% by weight, based on the total weight of solids, of a sticking agent or film-forming binder. 18. A transfer separator for carrying out the process of claim 1, wherein said transfer carrier is an impermeable, flexible web, said dried ultra-thin deposit lies over said web, said binder material of said deposit consisting essentially of microcrystalline cellulose or a mixture of microcrystalline cellulose with a small quantity of carboxy methyl cellulose. 19. A transfer separator according to claim 18, wherein the ultra-thin deposit also contains up to 35% by weight, based on the total weight of solids, of a sticking agent or film-forming binder.
This is a continuation-in-part of parent, copending application Ser. No. 442,070, filed Nov. 16, 1982. FIELD OF INVENTION The present invention relates to the coating of surfaces and, more particularly, the provision of abrasion-resistant coatings on various types of substrates by means of transfer coating or printing. BACKGROUND OF THE INVENTION U.S. Pat. Nos. 4,255,480; 4,263,081; 4,305,987; and 4,327,141 disclose embodiments which demonstrate abrasion-resistance enhancement of high and low pressure decorative laminates by providing an ultra-thin coating composed of mineral particles and microcrystalline cellulose on the surface of conventional decor paper, followed by impregnating the paper with melamine or polyester resin, and then using the decor paper in a normal laminating process but without the overlay paper. The resultant laminate exhibits abrasion-resistance qualities much better than those of conventionally produced high or low pressure decorative laminates containing an overlay layer. However, the embodiments illustrated in these patents are directed to the manufacture of abrasion-resistant high and low pressure laminates containing thermosetting resins, and there is no disclosure of the use of microcrystalline cellulose in combination with mineral particles in other environments, particularly for the protection of thermoplastic substrates. Moreover, the ultra-thin coating is applied to one of the elements, e.g. the decor sheet, which becomes part of the final laminate product. Transfer coating or printing, on the other hand, is well known. For example, there is a considerable body of prior art which shows coating compositions for use in transfer (hot stamp) applications to provide abrasion resistance to thermoplastic resin surfaces. Such heat transfers can include a layer containing inorganic grit particles to enhance abrasion resistance. As described in patents such as U.S. Pat. Nos. 3,666,516; 4,007,067; 3,770,479; 3,953,635; and 4,084,032, hot stamp tapes are often produced with the following layers, noting FIG. 1: A. Carrier Sheet or Web--such as films of polyester, cellophane, cellulose acetate, or paper. B. Primer Coat (optional)--to hold tick coat (see C.) to carrier sheet or web. C. Tick Coat (optional)--to impart a texture if desired. D. Release Coating (optional)--to enable release of subsequent coating from the above. E. Replicating Coat (optional)--to replicate the surface of the carrier sheet or web and surfaces of heretofore coated ticks. F. Abrasion Coat--to impart abrasion resistance. G. Color Coat--may be one coat or several to decorate the coating. H. Adhesion Coat--to enable the transferable portion of the composite to stick to the substrate. The hot stamp tape produced as described is then applied to a suitable substrate (adhesion coat against the substrate) under heat and pressure, and the carrier sheet or web with primer, tick and release coats, if applicable, are removed leaving the subsequent coats laminated onto the substrate, as shown in FIG. 1. These hot stamp tapes of the prior art typically do not offer suitable abrasion resistance to be used in environments of high traffic and abrasion. This deficiency has kept hot stamp tapes out of sizable markets. SUMMARY OF THE INVENTION The present invention is based on the discovery that the ultra-thin abrasion-resistant layers of the type disclosed in the aforementioned U.S. Pat. Nos. 4,255,480; 4,263,081; 4,305,987; and 4,327,141 provide enhanced abrasion resistance to a wide variety of both thermoplastic and thermosetting resin surfaces, and that coatings of this type can be transferred from one surface to another. It is an important feature of the present invention that when inorganic grit is compounded with a suitable binder material such as microcrystalline cellulose, much greater enhancement of abrasion resistance is obtained than in the prior transfer compositions containing equal amounts of inorganic grit. We have discovered that the ultra-thin abrasion-resistant coatings of the aforementioned U.S. Pat. Nos. 4,255,480; 4,263,081; 4,305,987; and 4,327,141 not only enhance abrasions resistance on thermosetting-type resins such as polyester and melamine-formaldehyde as disclosed in such patents, but also on thermoplastic-type resins such as acrylic and vinyl. We have also discovered that such ultra-thin (less than about 0.5 mils thick) abrasion-resistant coating need not be applied onto paper, which is subsequently resin impregnated and used in a laminating process, but that such a layer can be transfer coated in a variety of ways. Furthermore, we have found that enhanced abrasion resistance can be obtained on thermosetting and thermoplastic resins by transferring the dried ultra-thin coating to the plastic surface from a mold surface, or from a separator or release sheet during the molding or laminating process. Enhanced abrasion resistance using such an ultra-thin layer can also be achieved by transferring the layer plus thermosetting and/or thermoplastic resins as a composite from a carrier to a substrate, after which the carrier is subsequently discarded. We have also discovered that abrasion-resistance enhancement can be obtained using this coating in press cycles of very low pressure and duration. It is, accordingly, an object of the invention to overcome deficiencies in the prior art, such as pointed out and/or suggested above. It is another object of the invention to provide for the transfer coating of ultra-thin abrasion-resistant layers. It is another object of the invention to provide improved products of a great variety of materials, having improved abrasion-resistant surfaces. These and other objects and the nature and advantages of the instant invention will be more apparent from the following detailed description of specific embodiments, taken in conjunction with the drawing wherein: BRIEF DESCRIPTION OF THE DRAWING FIG. 1 is a typical prior art hot stamp tape, which may be modified to incorporate an ultra-thin abrasion-resistant layer in accordance with the instant invention; FIG. 2. is a schematic view showing a method for incorporating a grit coating into the surface of a substrate using a mold, according to a control process; FIG. 3 is a schematic view similar to FIG. 2, showing the transfer of an ultra-thin abrasion-resistant coating according to the invention from a mold surface into the upper surface of a substrate; FIG. 4 schematically shows a process similar to FIG. 2, except using a separator instead of a mold; FIG. 5 shows a process similar to FIG. 3 using an abrasion-resistant coating applied to a separator instead of to a mold, for transfer to a substrate; FIG. 6 is a schematic view of a hot stamp tape of simplified construction compared to that of FIG. 1, used for control comparisons in some of the following examples; FIG. 7 is a hot stamp tape of similar construction to the control tape of FIG. 6, but made in accordance with the present invention, FIG. 7 also schematically showing the transfer operation in process; FIG. 8, similar to FIG. 3, shows application of the invention to continuous lamination; and FIG. 9, similar to FIG. 3, shows application of the invention to another form of continuous lamination. DETAILED DESCRIPTION OF EMBODIMENTS The present invention is operable in a great variety of embodiments, and using a great variety of substrates, and the term "substrate" is used in a broad sense to mean any kind of body capable of receiving a transfer layer, whether the substrate be fibrous, thermoplastic, thermoset or thermosettable, wood, metal, particleboard, etc., it being understood that the transfer layer must bond to the substrate. The following examples are intended to illustrate, but not to limit, the various possibilities. I--Hot Stamp Tape (Heat Transferable Coatings) Hot stamp tape is a web of indeterminate length that carries thermally transferable material that is structured to provide an improved appearance, such as a woodgrain pattern, on a suitable substrate after transfer to the substrate, such as particleboard or the like, of transferable layers from the heat stamp web. Of course, the web can also be provided in sheet form. Inexpensive furniture is now made in this way. However, the surface of the product, which involves merely a particleboard backing with a thin woodgrain printed coating thereon, is not very durable and is easily abraded. Typically, a carrier web such as Mylar film is coated with a protective coating, then printed with woodgrain reproduction (normally three prints), and is then coated with an adhesive layer for bonding to the substrate. The construction is typically even considerably more complex, such as illustrated in FIG. 1. The so constructed heat transfer web or hot stamp tape is wound into rolls and sold to furniture companies who heat transfer the composite to particleboard or other substrate, the carrier sheet or web being discarded. The particleboard is thus decorated with a high quality woodgrain reproduction superior to direct wet printing on the particleboard. It eliminates a fairly involved process at the furniture manufacturer level, as well as solving fume problems which are becoming increasingly more difficult as environmental concerns become more predominate, and it also eliminates the need for highly skilled personnel. However, as noted above, the resultant product is not very abrasion-resistant as the top coating provides a NEMA (LD3.1980) abrasion resistance of only about twenty cycles. In addition, most applications require that the furniture manufacturer run the product through an additional coating and drying line. About seven billion square feet of wood veneer and wood reproductions are used by the furniture industry per year, and if a sufficiently abrasion-resistant product could be provided by transfer printing at a reasonable cost, it is estimated that a large fraction of this market could benefit from such a product. As is evidenced in Table 1, even the addition of aluminum oxide in relatively large quantity to resins typically used in the abrasion coat F (as mentioned in Dunning, U.S. Pat. No. 4,007,067) does not significantly increase the abrasion resistance of the product. Surprisingly though, with the use of the abrasion-resistant composition of U.S. Pat. Nos. 4,255,480; 4,263,081, and 4,305,987, and 4,327,141, the abrasion resistance of the hot stamp tape material is dramatically improved. Referring to Table 1, a series of trials were run to compare the relative abrasion resistances (as measured by the initial point of wear, NEMA LD3-3.01) of hot stamp tapes of various compositions. Each hot stamp tape composition differed in one way or another from all of the others. Different classes of resins were employed, i.e. thermosetting and thermoplastic types. Two types of thermoplastic resins were used, i.e. vinyl and acrylic. Two types of acrylic were used, i.e. Acrysol WS68 (Acrylic A)* and Rhoplex AC-61 (Acrylic B). One type of thermosetting resin was used, i.e. a butylated melamine-formaldehyde resin. The tapes used were basically of the construction shown in FIGS. 6 and 7. In each case a polyester carrier web was coated first with an aqueous top coat composition as set forth in Table 1, after which the top coat was dried at 250° F., the drying being carried out for periods of from 30 seconds to 90 seconds until the coating was dry to the touch. An aqueous base coat composition was then applied to the top coat and was dried under the same conditions. In Examples 3-10 and 12-14, the base coat also served as an adhesive layer. FIG. 6 shows control Examples 3-10, and FIG. 7 shows Examples 12-14. In Examples 11, 15 and 16 an additional coating was applied as an aqueous emulsion over the base coat, which additional coating after drying served as an adhesive coat; in Examples 11 and 16, this adhesive coat was Acrylic A, and in Example 15 it was Acrylic B as shown in Table 1., Consistent with U.S. Pat. Nos. 4,255,480; 4,263,081; 4,305,987 and 4,327,141, the ultra-thin top coat in Examples 12-14 must be dried at a temperature of at least 140° F. All hot stamps were transferred from the polyester film carrier (Melinex 377) onto mirror finish, high pressure decorative laminates used as substrates. So initial wear could be easily determined, the mirror surface of the laminates were decorated with a grid pattern before the transfer process. All thermoplastic transfers were made at pressing conditions of 325° F., 50 psi for 30 seconds and cooled to 90° F. while maintaining pressure. The butylated melamine transfers were made at 375° F., 750 psi for 3 minutes and cooled at 90° F. while maintaining pressure. The aluminum oxide used in all examples was the same. Control Examples 1-4 illustrate the initial wear values where only resins are used. Control Examples 5-11 show how the addition of aluminum oxide (44-50% by dry coat weight) into the top coat, exposed after transfer, affects abrasion resistance of the hot stamp tapes. The hot stamp tapes of Examples 12-15 were made with approximately the same amount of resin and aluminum oxide as each of the preceding examples, but the abrasion-resistant deposit (ARD) of the invention was the exposed coating after transfer. The Taber test was used to measure initial wear value. As can be seen from Table 1, the results are dramatic. Control Examples 1, 5 and 6 using Acrylic A gave an initial wear of only 75 cycles, even though control Examples 5 and 6 had a top coat containing, respectively 2.9 and 4.0 pounds per 3000 ft 2 of aluminum oxide. When the quantity of aluminum oxide was raised to 5.1 pounds per 3000 ft 2 in the top coat as shown in control Example 7, the initial wear doubled to 150 cycles. These poor values should be compared to Examples 12 and 13 according to the invention wherein initial wear values of more than 500 cycles and 450 cycles were obtained with only 4.6 pounds per 3000 ft 2 and 2.5 pounds per 3000 ft 2 aluminum oxide, respectively. Using a different resin system, namely Acrylic B, similar results were achieved. In control Example 2, without alumina, the initial wear was only 50 cycles. In Examples 8 and 9, having a top coat containing 3.5 and 5.6 pounds per 3000 ft 2 , respectively, of aluminum oxide, the initial wear increased to 100 and 200 cycles, respectively, still relatively poor performance. On the other hand, when using transfer ARD according to the invention as shown in Example 14 and using only 2.5 pounds per 3000 ft 2 of aluminum oxide, the initial wear value was 500 cycles. Using still a different resin, namely vinyl resin, again the results were similar. In control Example 3 using no alumina, the initial wear was only 50 cycles. In control Example 10, having a top coat containing 3.6 pounds per 3000 ft 2 of alumina, the initial wear value was 125 cycles. In Example 15 according to the invention, using an ARD top coat containing 4.6 pounds per 3000 ft 2 of alumina, the initial wear was 475 cycles; because the vinyl did not act as a good adhesion layer, the vinyl layer in Example 15 (and Example 16 as well as discussed below) was backed by an acrylic adhesion layer. The results with thermosetting resin were essentially the same. In control Example 4 the initial wear value was only 100 cycles. In control Example 11, having a top coat containing 3.7 pounds per 3000 ft 2 of alumina, the initial wear was 225 cycles. But in Example 16, in accordance with the invention, and using approximately 30% less alumina, i.e. 2.5 pounds per 3000 ft 2 in an ARD layer, the initial wear was 650 cycles. Hot stamp tapes are often transferred using heated nip rolls rather than the conventional pressing scheme used above. To simulate a heated nip roll operation, additional ARD coatings were transferred with heat and pressure application for 1 to 3 seconds and no cooling under pressure. Initial wear values comparable to those in Table 1 were achieved using this transfer method. TABLE 1__________________________________________________________________________EXAMPLENUMBER 1 2 3 4 5 6 7 8__________________________________________________________________________TOP ACRYL- ACRYLIC VINYL.sup.3 BUTYLATED.sup.4 ACRYLIC A ACRYLIC A ACRYLIC ACRYLIC BCOAT IC A.sup.1 B.sup.2 MELAMINE + + + + ALUMINA.sup.5 ALUMINA ALUMINA ALUMINATOP COAT 17.2 13.4 6.6 40.1 6.6 9.0 11.5 7.9WEIGHT(lb/ream)BASE ADHE- -- -- ACRYLIC ACRYLIC ACRYLIC ACRYLIC ACRYLIC ACRYLICSION COAT A A A A A BBASE/ADHE- -- -- 3.7 8.0 7.2 7.2 7.2 6.5SIONCOAT WEIGHT(lb/ream)TOTAL COAT 17.2 13.4 10.3 48.1 13.8 16.2 18.7 14.4WEIGHT(lb/ream)ALUM. OXIDE -- -- -- -- 2.9 4.0 5.1 3.5WT. (IN TOPCOAT-lb/ream)INITIAL WEAR 75 50 50 100 75 75 150 100VALUE(cycles) ← ← CONVENTIONAL TECHNOLOGY → →__________________________________________________________________________EXAMPLENUMBER 9 10 11 12 13 14 15 16__________________________________________________________________________TOP ACRYLIC B VINYL BUTYLATED ARD A.sup.6 ARD B.sup.7 ARD B ARD B ARD C.sup.8COAT + + MELAMINE ALUMINA ALUMINA + ALUMINATOP COAT 12.8 7.2 7.4 10.9 8.2 8.2 10.9 8.2WEIGHT(lb/ream)BASE/ADHE- ACRYLIC ACRYLIC BUT.MEL/ ACRYLIC ACRYLIC ACRYLIC VINYL/ BUT.MEL/SION COAT B B ACRYLIC A A A B ACRYLIC ACRYLIC ABASE/ADHE- 6.5 6.5 23.4/7.2 9.0 10.9 11.5 7.1/6.5 23.4/7.2SIONCOAT WEIGHT(lb/ream)TOTAL COAT 19.3 13.7 38.0 19.9 19.1 19.7 24.5 38.8WEIGHT(lb/ream)ALUM. OXIDE 5.6 3.6 3.7 4.6 2.5 2.5 4.6 2.5WT. (IN TOPCOAT-lb/ream)INITIAL WEAR 200 125 225 500+ 450 500 475 650VALUE(cycles) ← CONVENTIONAL TECHNOLOGY → ← PRESENT INVENTION →__________________________________________________________________________ .sup.1 ACRYSOL WS68 Rohm & Haas - thermosetting acrylic resin .sup.2 RHOPLEX AC61 Rohm & Haas - thermosetting acrylic resin .sup.3 VYNS3 Union Carbide .sup.4 CYMEL 1158 American Cyanamid - butylated melamineformaldehyde resin + 7.5% Polymerized Castor Oil GasChem - thermosetting resin .sup.5 ALUMINUM OXIDE, 30 micron Micro Abrasive Corp. .sup.6, 7, 8 See Table 2 II--Transfer ARD Formulations Table 2 below shows under the heading "ARD A" the basic ARD formula used in Example 12, above. This formulation is essentially the same as those disclosed in U.S. Pat. Nos. 4,255,480; 4,263,081; 4,305,9087; and 4,327,141. Details regarding the ARD composition are to be found in these patents, and such details are incorporated by reference. As can be seen from the initial wear value in Table 1, Example 12, above, abrasion resistance is excellent. However, due to handling techniques which are used in transfer coating, it has been found that handling is improved if a sticking aid or film forming binder is incorporated into the transfer ARD formulation. Any sticking agent that helps the ARD layer adhere to the carrier, such as a thermoplastic, a thermosetting resin, a gum, a colloid, etc., can be used. The quantity of the sticking agent is not critical at the lower end, but at the upper end one must be careful not to use so much sticking agent that the density of the alumina particles in the transfer ARD layer become so low that the abrasion-resistant properties of the ARD layer becomes significantly reduced, i.e. the ARD composition should not be diluted to the point where it is no longer effective. In general, one should use a minimum quantity of sticking agent or film forming binder sufficient to make the process work better; in general, this quantity, measured as solids, should not exceed about 10-35% by weight of the total quantity of solids in the ARD layer, although larger quantities may sometimes be desirable. Noting Table 2 below, it is seen that the other ARD examples contained as such sticking agent a small quantity of partially advanced melamine-formaldehyde resin or vinyl chloride which enabled better coating adhesion to the polyester film during the coating process. ARD F contains a larger than usual quantity of CMC which in this case serves as a film former. Use of such a sticking agent or film former reduces processing problems of flaking, insufficient wetting, and overcoating all relative to the carrier web. TABLE 2__________________________________________________________________________ ARD A ARD B ARD C ARD D ARD E ARD F__________________________________________________________________________H.sub.2 O 617 g 617 g 617 g 617 g 617 g 617 gCMC (carboxy methyl cellulose).sup.1 14.5 g 14.5 g 14.5 g 14.5 g 14.5 g 45 gMicrocrystalline Cellulose.sup.2 45 g 45 g 45 g 45 g 45 g 45 gAluminum Oxide.sup.3 45 g 45 g 45 g 45 g 45 g 45 gSilane.sup.4 3 g 3 g 3 g 3 g 3 g 3 gFormalin.sup.7 1.5 g 1.5 g 1.5 g 1.5 g 1.5 g 1.5 gMelamine resin -- 71 g 71 g -- 35 g --at 50% solids in H.sub.2 OTriton X-100.sup.5 -- -- 1.6 g -- -- --Vinyl Chloride Emulsion -- -- -- 71 g 35 g --at 50% solids in H.sub.2 O.sup.6__________________________________________________________________________ .sup.1 Grade 7L a product of Hercules Inc. .sup.2 Type RC591 a product of FMC Corp. .sup. 3 30 Micron a product of Micro Abrasives Corp. .sup.4 A1100 a product of Union Carbide Corp. .sup.5 A surfactant product of Rohm & Haas .sup.6 Geon 460 × 6 a product of B. F. Goodrich selfcrosslinkable PVC resin latex .sup.7 37% Formalin other preservatives may be used. The ARD composition may also desirably include a small amount of finely divided solid lubricant, such as micronized polyethylene wax, in accordance with copending U.S. application Ser. No. 508,629, filed June 28, 1983, in the name of O'Dell et al, hereby incorporated by reference, the solid lubricant being one which desirably melts during the transfer process. Such solid lubricant imparts scuff resistance to the final product. III--Mold Transfer Dramatically enhanced abrasion resistance can also be obtained on molded thermoplastic and thermosetting parts and products by transferring the abrasion-resistant coating from a mold to the plastic part surface during the molding process such as shown in FIG. 3. This process has wide utility in forming a great variety of products, and can be applied easily in any molding or laminating process wherein a mold or die surface is brought into contact under pressure against the plastic (thermoplastic or thermosetting resin) to be shaped or pressed. Thermoset products made in this way include laminates of various kinds, dinnerware, fiberglass impregnated products, automative and aircraft parts, housings, trays, boxes, helmets, etc. Thermoplastic products include, for example, vinyl floor tile, seat covers, wallpaper, shoes, transparent (e.g. acrylic) products, etc. Thermosetting Resin To illustrate that the above-mentioned approach yields unexpected results on melamine-formaldehyde resin, ARD C from Table 2 was coated at a rate of 8.7 lb/3000 ft 2 (˜2.8 lb/3000 ft 2 of grit) onto a mirror finish, chrome plated, stainless steel press plate, and dried at 250° F. This composite was pressed against a substrate of melamine-formaldehyde impregnated decor sheet (dry resin to decor paper ratio=0.5 to 1) backed by four phenol-formaldehyde impregnated kraft sheets. The press cycle was typical for high pressure decorative laminates. Bonding occurred during the flowing and curing of the melamine resin. As illustrated in Table 3, the abrasion resistance initial wear value was dramatically improved over the control (which had no abrasion-resistant coating). TABLE 3__________________________________________________________________________MOLD TRANSFER-MELAMINE (THERMOSETTING RESIN)(1000 psi, 300° F., 25 min. and cool) ARD DECOR PAPER #IMPREGNATED INITIAL WEAR COAT WEIGHT DRY RESIN TO PAPER KRAFT SHEETS VALUE (lb/ream) RATIO (190 lb/ream) (CYCLES)__________________________________________________________________________Control -- 0.5-1.0 4 20Transfer ARD 8.7 0.5-1.0 4 575__________________________________________________________________________ These results enable the production of overlay free, enhanced abrasion resistant laminate on continuous laminating equipment such as the Siempelkamp equipment, modified as generally shown in FIG. 8, and on single opening semi-continuous apparatus which is currently under development. Also, low pressure laminate with an ARD surface can be continuously made using the Hymenn equipment modified as shown in FIG. 9. Thermoplastic Resin Table 4 illustrates how ARD layers result in dramatic abrasion-resistance increases when transferred from mold surfaces onto thermoplastic type resins. Again, one vinyl and two different acrylic resins were used as examples. While Acrylic A is technically a product which sets upon application of heat, it is derived from or incorporates a thermoplastic and has many characteristics of thermoplastic resins and thus was used to simulate thermoplastics; the other two resins may also be curable upon the application of heat, but are believed to remain thermofusible, i.e. thermoplastic. TABLE 4__________________________________________________________________________MOLD TRANSFER - THERMOPLASTICS 1 2 3 4 5 6__________________________________________________________________________TOP COAT ACRYLIC A/ ACRYLIC B/ VINYL/ ARD C ARD B ARD D GRIT.sup.1 GRIT.sup.2 GRIT.sup.3TOP COAT WT. 15 10 8.5 14.8 8.7 8.7(lb/ream)BASE COAT ACRYLIC A ACRYLIC B VINYL- ACRYLIC A ACRYLIC B VINYL- ACRYLIC A ACRYLIC ABASE COAT WT. 34.5 34.5 9.3-17.4 34.5 34.5 15.7-17.4(lb/ream)GRIT WT. 6.6 4.2 6.9 4.8 2.8 2.8IN TOP COAT(lb/ream)PRESSING 325° F. 375° F. 375° F. 325° F. 375° F. 375° F.CONDITIONS 50 psi 750 psi 300 psi 50 psi 750 psi 300 psi 1 min. 2.5 min. 1 min. 1 min. 2.5 min. 1 min. & cool & cool & cool & cool & cool & coolINITIAL WEAR 150 200 150 600 600 425VALUE (cycles) ← CONTROLS → ← INVENTION → FIG. 2 FIG. 3__________________________________________________________________________ .sup.1 Acrysol WS68 Rohm & Haas Aluminum Oxide, 30 micron, Micro Abrasives Corp. .sup.2 Rhoplex AC61 Rohm & Haas Aluminum Oxide, 30 micron, Micro Abrasives Corp. .sup.3 Geon 460 × 6 B. F. Goodrich Aluminum Oxide, 30 micron, Micro Abrasives Corp. Examples 1, 2, and 3 are controls for the invention and were produced by coating the base coat, then top coat, onto textured finish high pressure decorative laminates, noting FIG. 2. The top coat contained resin/grit ratios of either 1.0 to 0.8 (both acrylic resins) or 1.0 to 1.0 (vinyl). These composites were then pressed against mirror finish chrome plated stainless steel molds under the same conditions that ARD was transferred onto corresponding composites in Examples 4-6. Examples 4, 5 and 6 were produced by coating the ARD onto the same mold used in Examples 1, 2 and 3, noting FIG. 3, an external mold release agent having first been coated onto the mold. The ARD was dried and then transferred from the mold to the respective thermoplastic resin which was previously coated onto textured, high pressure decorative laminates. Bonding resulted during the fusion and then solidification of the thermoplastic coating serving as the substrate. Note the grit weights for the controls (Examples 1, 2 and 3) are always greater than their ARD transfer equivalents (Examples 4, 5 and 6). Note also that in Examples 3 and 6, a pure vinyl coating was not used, i.e. we used acrylic as the coating against the laminate because the vinyl would not adhere well to the laminate surface. The resultant initial wear values presented in Table 4 show ARD increased the abrasion resistance of thermoplastic coatings by mold transfer. IV--Surface Separator Transfer ARD can also be transferred onto thermosetting and thermoplastic resins from a surface separator or release sheet. ARD is coated onto the surface separator or release sheet, dried and then transferred to the resin as shown in FIG. 5. As in the other transfer procedures described above using ARD in accordance with the instant invention, the surface onto which the ARD layer is transferred must become receptive, e.g. melted, during the transfer operation, for the ARD to adhere thereto, or there must be present a suitable adhesive layer by which the transfer ARD becomes adhered to the substrate. Thermosetting Resin To show how abrasion resistance of melamine resin is enhanced by ARD transfer from several types of surface separators during the molding operation, a set of runs were conducted (See Table 5). Different coats weights of ARD C formulation were applied to several types of surface separators and dried at 250° F. to touch. The surface separators used were: (1) Polypropylene film (2) Release agent coated glassine paper (3) Release agent coated foil-paper lamination (release coat on foil side). These surface separators with the dried ARD coatings thereon were then pressed against substrates of melamine resin impregnated decor papers of varying resin contents as shown in Column 2 of Table 5, it being understood that the ratio of 0.5-1.0 is the normal industrial resin/paper ratio for making high pressure laminate. The decor papers were reinforced by 4 sheets of phenolic impregnated kraft paper. Press cycles were varied in duration as shown in Table 5. Upon completion of the press cycles, the surface separators were removed from the composites. From Column 4 in Table 5, it is readily apparent that ARD dramatically increased the abrasion resistance of each composite. TABLE 5__________________________________________________________________________SURFACE SEPARATOR TRANSFER - THERMOSETTING RESIN(1000 psi, 295° F. peak) 2 3 4 1 DRY RESIN/ PRESS CYCLE INITIAL lbs/REAM DECOR PAPER TIME WEAR VALUE ARD Ct. Wt. WEIGHT RATIO (minutes) (cycles)__________________________________________________________________________Control FIG. 4 -- 0.5-1.0 25 20Polypropylene/ARD C 8.2 0.5-1.0 25 275Polypropylene/ARD C 10.9 0.5-1.0 25 450Glassine/ARD C 8.2 0.5-1.0 25 525Glassine/ARD C 10.9 0.5-1.0 25 550Paper-foil/ARD C 8.2 0.5-1.0 60 550Paper-foil/ARD C 8.2 0.7-1.0 60 650__________________________________________________________________________ Use of ARD transferred from surface separator for some applications of use is an improvement over the process shown in U.S. Pat. No. 4,255,480 because the coating does not have to be applied directly to the decor sheet, which is more expensive than the release sheets, resulting in lower cost from handling losses during the coating process. Scuff resistant products can also be made by this procedure using compositions as disclosed in the O'Dell et al copending application Ser. No. 508,629, filed June 28, 1983. Thus, an aqueous mixture is made up of 100 parts (dry weight) of ARD F and six parts by weight of Shamrock 394 micronized polyethylene wax. The mixture is coated on aluminum foil/paper parting sheet on the aluminum side, and also on parchment paper at the rate of 8.5 pounds/3000 ft 2 (dry solids weight), and the composition is dried at a temperature between 180° F. and the melting point of the polyethylene wax. After drying, both types of coated release paper are pressed in a normal cycle laminating procedure down on top of a solid color decor sheet saturated with melamine resin, beneath which is located a normal phenolic core. Standard press cycles of 800-1200 psi and 260°-300° F. are used. After cooling, the release paper is removed, and it is found that the coating has transferred to the melamine impregnated decor paper, and the resultant laminates are slippery and scuff resistant, as well as being abrasion resistant. The procedure described immediately above can also be carried out to produce a scuff-resistant product without enhanced abrasion resistance using a mixture of microcrystalline cellulose and hydroxymethyl cellulose as binder material for finely divided solid lubricant. Or other binder material such as sodium alginate (Kengin LV) may be used in place of the microcrystalline cellulose. Thus, an aqueous emulsion of 6 parts by weight Kelgin and 6 parts by weight Shamrock 394 in 300 parts of water is coated on the aluminum side of aluminum/foil paper parting sheet on parchment paper at the rate of 1.5-2 lbs./3000 ft 2 (dry weight) and processed as described above. The resultant laminates are slippery and scuff-resistant. Thermoplastic Resins ARD also can be transferred from surface separators (e.g. foil/paper laminate) onto thermoplastic resins, e.g. vinyl coated wallpaper. FIG. 5 shows this process using low transfer pressure. The only difference between this and the mold transfer process described earlier is the substitution of a surface separator for the mold. The results of the experiments with surface separators are set forth in Table 6. Again, while one or more of the products used are technically heatsetting, they are derived from thermoplastics and have many thermoplastic properties and were used for sake of convenience. TABLE 6__________________________________________________________________________SURFACE SEPARATOR TRANSFER - THERMOPLASTICS 1 2 3 4 5 6__________________________________________________________________________TOP COAT ACRYLIC A/ ACRYLIC B/ VINYL/ ARD C ARD C ARD E GRIT.sup.1 GRIT.sup.2 GRIT.sup.3TOP COAT WT. 10 14.5 13.8 8.7 9.5 8.7(lb/ream)BASE COAT ACRYLIC A ACRYLIC B VINYL- ACRYLIC A ACRYLIC B VINYL- ACRYLIC A ACRYLIC ABASE COAT WT. 34.5 21.5 9.3-17.4 34.5 21.5 15.7-17.4(lb/ream)GRIT WT. 4.2 6.2 6.9 2.8 3.0 2.8IN TOP COAT(lb/ream)PRESSING 325° F. 375° F. 375° F. 325° F. 375° F. 375° F.CONDITIONS 50 psi 750 psi 300 psi 50 psi 750 psi 300 psi 1 min. 2.5 min. 1 min. 1 min. 2.5 min. 1 min. & cool & cool & cool & cool & cool & coolINITIAL WEAR 175 200 150 525 400 675VALUE (cycles) ← CONTROLS → ← INVENTION → FIG. 4 FIG. 5__________________________________________________________________________ .sup.1 Acrysol WS68 Rohm & Haas Aluminum Oxide, 30 micron, Micro Abrasives Corp. .sup.2 Rhoplex AC61 Rohm & Haas Aluminum Oxide, 30 micron, Micro Abrasives Corp. .sup.3 Geon 460 × 6 B. F. Goodrich Aluminum Oxide, 30 micron, Micro Abrasives Corp. It will be obvious to those skilled in the art that various changes may be made without departing from the scope of the invention and the invention is not to be considered limited to what is shown in the drawing and described in the specification.

Description

Topics

Download Full PDF Version (Non-Commercial Use)

Patent Citations (6)

    Publication numberPublication dateAssigneeTitle
    US-2941916-AJune 21, 1960Meyercord CoHeat resistant decalcomania transfer and method of making and using the same
    US-3770479-ANovember 06, 1973Thermark CorpHot stamp tape with etched carrier
    US-4007067-AFebruary 08, 1977Avery Products CorporationMethod for making and using hot stamp tape
    US-4101698-AJuly 18, 1978Avery International Corp.Elastomeric reflective metal surfaces
    US-4305987-ADecember 15, 1981Nevamar CorporationAbrasion resistant laminate
    US-4392901-AJuly 12, 1983Pernicano Vincent S, Wright Michael RReflective garment and method of manufacturing same

NO-Patent Citations (0)

    Title

Cited By (99)

    Publication numberPublication dateAssigneeTitle
    US-2006174556-A1August 10, 2006Pergo (Europe) AbFloor strip
    US-2008168729-A1July 17, 2008Pfleiderer Schweiz AgTransitions having disparate surfaces
    US-2011151193-A1June 23, 2011Cantley Richard W, Kokotovich Nick MArticle with inverse wood grain pattern
    US-6555216-B2April 29, 2003Mannington Mill, Inc.Contrasting gloss surface coverings optionally containing dispersed wear-resistant particles and methods of making the same
    US-2007245662-A1October 25, 2007Pergo (Europe) AbTransition molding and installation methods therefor
    US-7026038-B2April 11, 2006Nevamar Company, LlcWear resistant laminates
    US-2004191547-A1September 30, 2004Frank OldorffProcess for finishing a wooden board and wooden board produced by the process
    US-6114008-ASeptember 05, 2000Mannington Mills, Inc.Surface coverings having a natural appearance and methods to make a surface covering having a natural appearance
    US-2005150182-A1July 14, 2005Pergo (Europe) AbTransition molding
    US-7207143-B2April 24, 2007Pergo (Europe) AbTransition molding and installation methods therefor
    US-5456949-AOctober 10, 1995Formica Technology Inc.Method of producing damage resistant decorative laminate
    US-9032685-B2May 19, 2015Pergo (Europe) AbFlooring panel or wall panel and use thereof
    US-5728797-AMarch 17, 1998International PaperMethod of making cured resin particles
    US-8528285-B2September 10, 2013Pergo (Europe) AbJoint cover assembly and kit comprising this joint cover assembly as well as installation method thereof
    US-5558906-ASeptember 24, 1996Formica Technology Inc.Wear-resistant decorative laminates and methods of producing same
    US-7678425-B2March 16, 2010Flooring Technologies Ltd.Process for finishing a wooden board and wooden board produced by the process
    US-6436159-B1August 20, 2002Lilly Industries, Inc.Abrasion resistant coatings
    US-5019440-AMay 28, 1991Toyo Ink Manufacturing Co., Ltd.Decorative plate
    US-6440538-B1August 27, 2002Lg Chem Ltd.Abrasion resistant laminate
    US-7559177-B2July 14, 2009Pergo (Europe) AbSmooth flooring transitions
    US-9464443-B2October 11, 2016Pergo (Europe) AbFlooring material comprising flooring elements which are assembled by means of separate flooring elements
    US-5961903-AOctober 05, 1999Mannington Mills, Inc.Method of making a surface covering having a natural appearance
    US-4774035-ASeptember 27, 1988Camelot Industries CorporationProcess of coating an ophthalmic lens
    US-9677285-B2June 13, 2017Pergo (Europe) AbBuilding panels
    US-8661762-B2March 04, 2014Pergo (Europe) AbFlooring panel or wall panel and use thereof
    US-6001207-ADecember 14, 1999Avery Dennison CorporationThermoformable conductive laminate and process
    US-9316006-B2April 19, 2016Pergo (Europe) AbBuilding panels
    US-5362557-ANovember 08, 1994Formica Technology Inc.Wear resistant decorative laminates comprising mineral particles and methods for producing same
    US-9322162-B2April 26, 2016Pergo (Europe) AbGuiding means at a joint
    US-8448399-B2May 28, 2013Pergo (Europe) AbFloor strip
    US-2010242393-A1September 30, 2010Sven KornfaltJoint cover assembly and kit comprising this joint cover assembly as well as installation method thereof
    US-7150134-B2December 19, 2006Pergo (Europe) AbFloor strip
    US-7384697-B2June 10, 2008Mannington Mills, Inc.Surface coverings containing aluminum oxide
    US-5686186-ANovember 11, 1997Avery Dennison CorporationThermoformable conductive laminate and process
    US-2008063844-A1March 13, 2008Mannington Mills, Inc.Surface coverings containing aluminum oxide
    US-RE34743-ESeptember 27, 1994Toyo Ink Manufacturing Co., Ltd.Decorative plate
    US-8003168-B2August 23, 2011Kronotec AgMethod for sealing a building panel
    US-8793954-B2August 05, 2014Pergo (Europe) AbTransition molding
    US-2010307677-A1December 09, 2010Carsten BuhlmannMethod for producing a decorative laminate
    US-2004180181-A1September 16, 2004Eric Franzoi, Scott Laprade, Srikanth PrasadWear resistant laminates
    US-2004026017-A1February 12, 2004Taylor Dene H., Hardesty Jon H., Daniels Evan R.Method and system for producing a wood substrate having an image on at least one surface and the resulting wood product
    US-8631623-B2January 21, 2014Pergo (Europe) AbSet of panels comprising retaining profiles with a separate clip and method for inserting the clip
    US-8484919-B2July 16, 2013Pergo (Europe) AbTransitions having disparate surfaces
    US-9611656-B2April 04, 2017Pergo (Europe) AbBuilding panels
    US-6291078-B1September 18, 2001Mannington Mills, Inc.Surface coverings containing aluminum oxide
    US-7014802-B1March 21, 2006Mannington Mills, Of Delaware, Inc.Methods to make a surface covering having a natural appearance
    RU-2587155-C2June 20, 2016Ивс Н.В.Method for producing plate-shaped product and plate-shaped product
    US-2004206038-A1October 21, 2004Oliver StanchfieldSmooth flooring transitions
    US-8875465-B2November 04, 2014Pergo (Europe) AbFlooring panel or wall panel and use thereof
    US-8327595-B2December 11, 2012Pergo (Europe) AbTransition molding
    US-4925514-AMay 15, 1990Mitsubishi Rayon Company, Ltd.Light attenuator and process for fabrication thereof
    US-6964722-B2November 15, 2005Trio Industries Holdings, L.L.C.Method for producing a wood substrate having an image on at least one surface
    US-2005235593-A1October 27, 2005Hendrik HechtFlooring panel
    US-8257791-B2September 04, 2012Kronotec AgProcess of manufacturing a wood fiberboard, in particular floor panels
    US-7665262-B2February 23, 2010Integritect Consulting, Inc.Composite bevel siding
    US-2006196135-A2September 07, 2006Pergo (Europe) AbTransition molding
    US-2002160680-A1October 31, 2002Laurence Kenneth John, Drees Terry Paul, O'brien Kevin Francis, Fairbanks Robert P.Decorative laminate assembly and method of producing same
    US-5380390-AJanuary 10, 1995Ultimate Abrasive Systems, Inc.Patterned abrasive material and method
    US-6753066-B2June 22, 2004Mannington Mills Of Delaware, Inc.Surface coverings having a natural appearance and methods to make a surface covering having a natural appearance
    US-6803110-B2October 12, 2004Formica CorporationDecorative laminate assembly and method for producing same
    US-8176698-B2May 15, 2012Kronotec AgPanel
    US-6093473-AJuly 25, 2000Lg Technology Sales And Marketing, Inc.Abrasion resistant laminate and method for making same
    US-2007193172-A1August 23, 2007Pergo (Europe) AbTransition molding
    US-8578675-B2November 12, 2013Pergo (Europe) AbProcess for sealing of a joint
    US-2004258907-A1December 23, 2004Pergo (Europe) AbProcess for the production of a floor strip
    US-6898911-B2May 31, 2005Pergo (Europe) AbFloor strip
    US-5490893-AFebruary 13, 1996Avery Dennison CorporationThermoformable conductive laminate and process
    US-9534397-B2January 03, 2017Pergo (Europe) AbFlooring material
    US-9260869-B2February 16, 2016Pergo (Europe) AbBuilding panels
    US-5288540-AFebruary 22, 1994Formica Technology DelawareDamage resistant decorative laminate having excellent appearance and cleanability and methods of producing same
    US-9115500-B2August 25, 2015Pergo (Europe) AbSet of panels comprising retaining profiles with a separate clip and method for inserting the clip
    US-7735283-B2June 15, 2010Pergo AGTransition molding and installation methods therefor
    US-7749596-B1July 06, 2010International Paper CompanyEngineered crack-resistant paper and board
    US-8544233-B2October 01, 2013Pergo (Europe) AbBuilding panels
    US-7065931-B2June 27, 2006Pergo (Europe) AbFloor strip
    US-8539731-B2September 24, 2013Pergo (Europe) AbTransition molding and installation methods therefor
    US-6641629-B2November 04, 2003Eugen Safta, Frank Bor-Her Chen, Harvey Richard Forrest, Gregory David MuselmanAbrasion resistant coatings
    US-6265082-B1July 24, 2001Kevin L. Dunham, John C. TsirovasilesFire retardant compositions and methods for their preparation and use
    US-9255414-B2February 09, 2016Pergo (Europe) AbBuilding panels
    US-9174423-B2November 03, 2015Surface Technologies Gmbh & Co. KgMethod for producing a decorative laminate
    US-2005144881-A1July 07, 2005Pergo (Europe) AbMolding and flooring material
    US-6482337-B1November 19, 2002Ricoh Company, Ltd.Method for evaluation of abrasion of a forming mold
    US-9464444-B2October 11, 2016Pergo (Europe) AbSet of panels comprising retaining profiles with a separate clip and method for inserting the clip
    US-2003154678-A1August 21, 2003Oliver StanchfieldTransition molding
    US-2003159389-A1August 28, 2003Sven Kornfalt, Per Bengtsson, Hans Sjolin, Oliver StanchfieldFloor strip
    US-8615952-B2December 31, 2013Pergo (Europe) AbSet of panels comprising retaining profiles with a separate clip and method for inserting the clip
    US-7081300-B2July 25, 2006Formica CorporationDecorative laminate assembly and method of producing same
    US-2005217193-A1October 06, 2005Pergo (Europe) AbFloor strip
    US-7883597-B2February 08, 2011Integritect Consulting, Inc.Composite bevel siding
    US-2005003149-A1January 06, 2005Pergo (Europe) AbFloor strip
    US-8016969-B2September 13, 2011Flooring Technologies Ltd.Process for finishing a wooden board and wooden board produced by the process
    US-7640705-B2January 05, 2010Pergo (Europe) AbFloor strip
    US-2006201093-A1September 14, 2006Pergo (Europe) AbTransition molding and installation methods therefor
    US-9593491-B2March 14, 2017Pergo (Europe) AbSet of panels
    US-7820287-B2October 26, 2010Pergo AGProcess for the production of a floor strip
    US-6860074-B2March 01, 2005Pergo (Europe) AbTransition molding
    US-7790293-B2September 07, 2010Flooring Technologies Ltd.Process for finishing a wooden board and wooden board produced by the process
    US-7640706-B2January 05, 2010Pergo (Europe) AbTransition molding
    US-8978334-B2March 17, 2015Pergo (Europe) AbSet of panels